PHYSICAL PROPERTIES:

Poly 15-3 & 15-3X Poly 15-6 Poly 15-8 Poly 1510 Poly 1512 & 1512X Poly 1512 Clear Mix ratio, by weight 1A to 1B 1A to 1B 26A to 100B 1A to 1B 1A to 1B 1A to 1B Hardness, Shore D 80 72 70 71 71 71 Pour time, 1 lb. mix 15 min. (Poly 15-3) 5 min. 30 min. 19 min. 22 min. (Poly 1512) 22 min. (faster with Part X) 5 min. (Poly 15-3X)       5 min. (Poly 1512X)   Maximum exotherm, 1 lb. mass 50oC 95oC 55oC 129oC 122oC 122oC Demold time 12 hrs. (Poly 15-3) 1 to 3 hrs. 1 to 16 hrs. 1 to 16 hrs. 1 to 16 hrs. (Poly 1512) 1 to 16 hrs. (faster with Part X) 1 hr.   (Poly 15-3X)       30 min. (Poly 1512X)   Specific gravity, g/cc 1.53 1.08 1.57 1.08 1.10 1.10 Color, cured low Tan Tan Gray Off White White Clear/Slig ht Yellow Viscosity, 2 min. after mixed 2,000 cps. 800 cps. 6,000 cps. 160 cps. 400 cps. 400 cps. Specific Volume, cu. inches/lb. 18 26 17.6 26 25.1 25.1 Shrinkage during cure, inches per inch 0.0002* (Poly 15-3) 0.003* 0.0002 Very low* Very low* Very low* *Shrinkage is primarily caused by gelling while hot then cooling. Parts that cure with minimal temperature rise will exhibit minimal shrinkage.

PACKAGING:

Containers                  Size Net lbs. Product Weight/lbs.   A    B    A    B  POLY 15-3, 15-3X Mix Ratio 1A to 1B 5 1 qt. 1 qt. 2.5 2.5 20 1 gal. 1 gal. 10.0 10.0 100 5 gal. 5 gal. 50.0 50.0             POLY 15-6, 1510, 1512, 1512X, 1512 Clear Mix Ratio 1A to 1B 4 1 qt. 1 qt. 2.0 2.0 16 1 gal. 1 gal. 8.0 8.0 80 5 gal. 5 gal. 40.0 40.0 900 55 gal. 55 gal. 450.0 450.0               POLY 15-8 Mix Ratio 26A to 100B 3.2 1 pt. 1 qt.   0.7 2.5 12.1 1 qt. 1 gal.   2.5 9.6 48.5 1 gal. 5 gal.   10.0 38.5               Part 15X Catalyst: 1 oz., 1 pt. (1.0 lb.), 1 gal. (8.0 lbs.), 5 gal. (40.0 lbs.) Part 15F Foamer:  1 oz., 1 pt. (1.0 lb.), 1 gal. (8.0 lbs.), 5 gal. (40.0 lbs.) Bronze Powder:    2 lb. can, 10 lb. can, 110 lb. can Poly Fiber:              2 lb. bag Pol-Ease® 2300 Release Agent:  12 oz. can, Case of 12 cans

Close Window