PlatSil® SiliGlass Silicone Rubber
Type: Platinum-Cured Silicone Rubber
Shore Hardness: A40
Mix Ratio: 1A:1B by weight or volume
Pour Time: 7 Minutes
Demold Time: 30 Minutes
Color: Clear
NOTE: SiliGlass is designed to act and look like broken glass.

TinSil® 70-11 Silicone Rubber
Type: Tin-Cured Silicone Rubber
Shore Hardness: A10
Mix Ratio: 1A:10B
Pour Time: 45 Minutes
Demold Time: 16 Hours
Color: Blue

TinSil® 70-20 Silicone Rubber
Type: Tin-Cured Silicone Rubber
Shore Hardness: A20
Mix Ratio: 1A:10B
Pour Time: 60 Minutes
Demold Time: 16 Hours
Color: Blue

TinSil® 70-25 Silicone Rubber
Type: Tin-Cured Silicone Rubber
Shore Hardness: A25
Mix Ratio: 1A:10B
Pour Time: 60 Minutes
Demold Time: 16 Hours
Color: Blue

TinSil® 70-60 Silicone Rubber
Type: Tin-Cured Silicone Rubber
Shore Hardness: A60
Mix Ratio: 5A:100B
Pour Time: 30 Minutes
Demold Time: 24 Hours
Color: Red
NOTE: This rubber is stable at high temperatures making it suitable for casting low-melting metals (it has very low tear strength because of its hardness).

TinSil® 80-15 Silicone Rubber
Type: Tin-Cured Silicone Rubber
Shore Hardness: A15
Mix Ratio: 1A:10B
Pour Time: 30 Minutes
Demold Time: 24 Hours
Color: Peach

TinSil® 80-40 Silicone
Rubber Type: Tin-Cured Silicone Rubber
Shore Hardness: A40
Mix Ratio: 1A:10B
Pour Time: 45 Minutes
Demold Time: 24 Hours
Color: Peach

TinSil® Brush/Spray 25 Silicone Rubber
Type: Thixotropic Tin-Cured Silicone Rubber
Shore Hardness: A25
Mix Ratio: 1A:10B
Pour Time: 60 Minutes
Demold Time: 16 Hours
Color: Milky White

TinSil® Gel-10 Silicone Rubber
Type: Tin-Cured Silicone Rubber
Shore Hardness: A10
Mix Ratio: 1A:10B
Pour Time: 45 Minutes
Demold Time: 16 Hours
Color: Translucent